Cold Forming Plastic Sheet

It is also a shape memory polymer which will return to its original flat form on application of moderate heat such as immersion in very hot water.

Cold forming plastic sheet. Spectar supposedly looks and handles much like acrylic but with the surprising property that it can be cold formed without breaking or whitening and exhibits a memory effect holding a cold bend until reheated. In this procedure after heating the polycarbonate sheet to its forming temperature the sheet is lowered to the mold followed by the plug. Polycarbonate is good for cold working. Cold forming plexiglas sheet can be cold formed bent at room temperature in a smooth arc and held to a radius by forcing the material into a curved channel support.

This is a type of vacuum forming where thin or thick gauge plastic sheet is placed over a die heated to a temperature that allows the material to become pliable then is stretched over the surface of the die while vacuum pressure pulls the sheet down and into its final shape. It sandwiches the sheet between the mold and the plug. Amorphous plastics like abs and polycarbonate generally have wide processing windows and good melt strength making them easy to thermoform. Modify the timing as necessary.

Uk educational supply center centre mindsets online sells variously sized 3mm thick sample sheets of eastman s spectar copolyester at not completely outlandish prices. The only major variable that can affect the forming process is the thickness of the plastic sheet. It can be formed into a permanent shape without heating avoiding the use of ovens or strip heaters. For thicker sheets it will take longer and for thinner sheets it will take less time.

It can also shorten the time required to transport the heated sheet from the oven to the forming equipment thus minimizing the possibility of cold forming. The design of the unit permits the operator to open all the clamps at once by simply opening a valve on the air line. Cold formed plastic cfp looks like acrylic but has a toughness approaching polycarbonate. This article uses a sheet about 1 4 thick so all times are about 10 to 15 minutes per step.

The recommended radius of curvature should be a value greater than 180 times the thickness of the sheet for plexiglas g sheet and 300 times the thickness for plexiglas mc sheet see table below recommended minimum radii of curvature for cold formed plexiglas sheetnominal sheet thickness recommended. Any of the amorphous sheet plastics can be heated and formed. Thermoforming is useful for clamshell packaging. Clamping and unclamping sheets preparatory to forming.